CARATTERIZZAZIONE MECCANICA DI PROVINI SANDWICH IBRIDI REALIZZATI MEDIANTE ADDITIVE MANUFACTURING CON CORE IN ALSI10MG E PELLI IN CFRP

This thesis investigates the use of active infrared thermography for detecting defects in sandwich panels with carbon-fiber skins and an aluminum core. The Step, Lock-In, and TSA techniques made it possible to identify and quantify debonding at the skin–core interface, highlighting a correlation between defect size and the reduction in flexural strength obtained from mechanical characterization tests performed according to standards. The results show that thermography is a fast and non-invasive method for assessing the integrity of sandwich structures, with potential applications in quality control and industrial diagnostics.

Il lavoro di tesi analizza l’utilizzo della termografia infrarossa attiva per l’individuazione di difetti in pannelli sandwich con pelli in fibra di carbonio e anima in alluminio. Le tecniche Step, Lock-In e TSA hanno permesso di rilevare e quantificare scollamenti all’interfaccia pelle–anima, evidenziando una correlazione tra l’estensione dei difetti e la riduzione della resistenza a flessione ricavate dalle prove di caratterizzazione meccanica, eseguite secondo normativa. I risultati dimostrano che la termografia rappresenta un metodo rapido e non invasivo per la valutazione dell’integrità di strutture sandwich, con potenziali applicazioni nel controllo di qualità e nella diagnostica industriale.