ANALISI STRUTTURALE DI BOTTIGLIE DI LATTE IN POLIETILENE AD ALTA DENSITÀ

This thesis was carried out during a six-month internship at the PIMM Laboratory in Paris, as part of the Double Degree Programme at the École Nationale Supérieure d'Arts et Métiers ParisTech University. It was aimed at the structural analysis of high-density polyethylene milk bottles made by the French company Logoplaste, which present cracks at high-stress areas (bottom of the bottle, handle, etc.), generated during the batch storage phase. Through an initial study of the microstructure and mechanical properties, followed by an analysis of the aging process of the bottles, the origins of these surface defects are studied.

Il lavoro di tesi è stato realizzato durante il tirocinio della durata di sei mesi presso il Laboratorio PIMM di Parigi, previsto dal Programma di Double Degree alla Università École Nationale Supérieure d'Arts et Métiers ParisTech. È stato finalizzato alla analisi strutturale di bottiglie di latte in polietilene ad alta densità realizzate dall'azienda francese Logoplaste, le quali presentano cricche in corrispondenza di zone ad alta concentrazione di stress (fondo della bottiglia, manico etc.) , generate durante la fase di stoccaggio in lotti. Attraverso un iniziale studio della microstruttura e delle proprietà meccaniche, seguito da un'analisi del processo di invecchiamento delle bottiglie, si studiano le origini di tali difetti superficiali.